Metall- und Materialverarbeitung – Häufig gestellte Fragen

Carbon steel components have been routinely annealed or heat treated in nitrogen-hydrogen based atmospheres to relieve stress, alter microstructure and/or improve surface appearance for a number of years. The flow rate and composition of the atmosphere to be used for annealing components in furnaces are usually determined by a trial and error approach.

Although the composition of nitrogen-hydrogen based atmosphere introduced into a furnace does not change with time, the true reducing or oxidiing potential of the atmosphere inside the furnace changes continuously with time due to leaks and drafts in the furnace, desorption of impurities such as moisture from the surface of components or decomposition of lubricant present on the surface of components being annealed. 

The green color that you see on stainless steel parts is chromium oxide (Cr₂O₃). It forms when there is too much oxygen and/or moisture in the furnace atmosphere, which is usually caused by a water leak, poor atmosphere tightness, or overly low flow rates of atmosphere gas. A dark green-brown color indicates significant levels of free oxygen inside the furnace originated by a large air leakage.

In addition to the traditional steel and copper test, some companies run a piece of stainless through the furnace to check for high moisture and oxygen levels. A better and more precise way of measuring moisture and oxygen levels is to install an oxygen analyzer and dew point meter. It's inexpensive and highly accurate. If a green oxide film is forming on your stainless steel parts, that's an indication that the furnace or atmosphere is not optimized.

Dezincification is typically defined as the leaching of zinc from copper alloys in an aqueous solution. In thermal processing of brasses (and other zinc-containing alloys), dezincification is the removal of zinc from the metal substrate during thermal processes, like brazing and annealing, typically due to the very low vapor pressure of zinc in the alloys. Dezincification can result in excessive furnace dusting, zinc vapors alloying with other metals, and in extreme cases, loss of alloy properties.

While eliminating dezincification is not always possible, it can be reduced during thermal processing. Controlling temperature, time at temperature, and the furnace atmosphere's reducing potential can help minimize dezincification and improve your thermal processing. However, understanding which variables to change can be a challenge. Air Products' industry specialists, experienced in thermal processing, can help pinpoint the variable(s) that you can regulate to help lower costs and improve productivity by minimizing dezincification.

Bright annealing of steels requires conditions that are reducing to steel oxides. Traditionally, the Ellingham diagram has been used to predict the conditions that correspond to oxidation of pure metals or reduction of their oxides. This method can be used to predict the conditions that should be reducing to iron oxides and the oxides of the alloying elements added to steels, such as chromium oxide when stainless steels are considered. This traditional approach is not precise because it only uses thermodynamic data for pure metals and their oxides—it ignores the fact that iron and alloying elements form a solid solution. In addition, you can only determine the approximate equilibrium partial pressure ratio of hydrogen and water vapor for oxidation of a specific metal at a particular temperature.